In the moving parts, because of long-term friction caused by the wear of parts, when the shaft and hole clearance wear to a certain extent must be replaced parts, so the designer in the design of the lower hardness, better wear resistance material for the shaft sleeve or bushing, so as to reduce the wear of the shaft and seat.s
We can offer a wide range of components for:
All sizes can be customized, Can be made into various of complex shapes, high dimension accuracy.
The main characteristics of the alumina ceramic products
1. They offer different grade dimensional accuracy per sintered only, precision machining
2. They are more cost-effective ceramic parts with equivalent performance among all other technical ceramics
3. High hardness, it is can be up to 1700 HV, and Super compressive strength up to 2240 Mpa
4. High heat resistance: Alumina ceramic parts offer excellent thermal stability, which means that it is widely used in areas where resistance to high temperatures is essential.
5. Good wear resistance: it is an ideal choice to wear pants in the high abrasive industry
6. High electrical resistivity: used in all-electric products, electric heating products, and wear-resistant machinery parts.
7. High corrosion resistance: It is insoluble in water and only slightly soluble in strong acid and alkaline solutions. Good chemical stability of alumina leads to high corrosion resistance.
8. We support a variety of customized alumina ceramic parts base on customer's drawing, sample, or reference parameters
Application of alumina ceramic parts
Remark:
Alumina ceramic parts are widely used in the electronic, electrical, machinery, chemistry, ceramic seal, mineral, new energy, military, aerospace, almost all modern industries.
Datasheet of technical ceramic materials
| Property | Units | Materials | ||||
| 99.5%Al2O3 | 99%Al2O3 | 95%Al2O3 | ZrO2 | Si3N4 | ||
| Density | g/cm3 | ≥3.85 | ≥3.80 | ≥3.60 | ≥6.0 | ≥3.2 |
| Water absorption | % | 0 | 0 | 0 | 0 | 0 |
| Hardness | HV | 1700 | 1700 | 1500 | 1300 | 1550 |
| Flexural strength | Mpa | ≥379 | ≥338 | ≥320 | ≥1200 | ≥600 |
| Compressive strength | Mpa | ≥2240 | ≥2240 | ≥2000 | ≥1990 | ≥2500 |
| Fracture toughness | Mpa m1/2 | 4-5 | 4-5 | 3-4 | 6.5-8 | 6 |
| Max. service temperature (Non-loading) |
ºC | 1675 | 1600 | 1500 | 1000 | 1200 |
| CTE (20-800ºC) | 1×10 -6 /ºC | 6.5~8.0 | 6.2~8.0 | 5.0~8.0 | 8.0~9.5 | 3.1 |
| Thermal shock | T(ºC) | ≥250 | ≥200 | ≥220 | ≥300 | ≤1000 |
| Thermal conductivity(25ºC) | W/m.k | 30 | 29 | 24 | 3 | 15~20 |
| Volume resistivity (25ºC ) | ohm.cm | >1 x 10 14 | >1 x 10 14 | >1 x 10 14 | >1 x 10 11 | >1 x 10 12 |
| Insulation strength | KV/mm | 19 | 18 | 18 | 17 | |
| Dielectric constant(1Mhz) | (E) | 9.7 | 9.5 | 9.5 | 29 | |